选择优创的理由POM典型应用产品特点及物性产品参数性能项目试验条件[状态]测试方法测试数据数据单位其它性能弯曲降服强度+73℉ASTM D-79014.3MPsi基本性能密度ASTM D-7921.42物理性能吸水量Equil.50%R.h.+73℉(+23℃)ASTM D-5700.22%吸水量24hrs浸泡+73℉(+23℃)ASTM D-5700.25%吸水量浸泡均衡点+73℉(+23℃)ASTM D-5700.90%扩散因数+73℉(+23℃)106HzASTM D-1500.005机械性能摩擦系数+73℉(+23℃)动态ThrustWasherTest30.35挠曲系数+70℃在25℃下1550MPa挠曲系数-55℃在25℃下3650MPa断裂时之拉力伸张度+73℉(+23℃)ASTM D-63875%挠曲系数+158℉在25℃下225MPsi伸张强度+212℉ASTM D-6385.2MPsi断裂时之拉力伸张度+212℉(+100℃)ASTM D-638>260%IZOD冲击强度+73℉ASTM D-2562.3ft.lb/in伸张强度+250℉ASTM D-6383.8MPsi伸张强度-68℉ASTM D-63814.7MPsi挠曲系数+212℉在25℃下130MPsi挠曲系数-68℉在25℃下530MPsi挠曲系数+250℉在25℃下90MPsi拉力冲击抵抗力+73℉D1822Long170ft.lb/in2拉力冲击抵抗力+23℃D1822Long350kj/m2剪力+23℃ASTM D-73265.5MPa挠曲系数+73℉在25℃下380MPsi剪力+73℉ASTM D-7329.5MPsi挠曲系数+100℃25℃下895MPa弯曲疲劳忍耐限度+73℉ASTM D-6714.7MPsi伸张强度+100℃ASTM D-63835.9MPa断裂时之拉力伸张度+250℉(+122℃)ASTM D-638>260%断裂时之拉力伸张度+158℉(+70℃)ASTM D-638230%无切口冲击程度+73℉ASTM D-256>100(no break)ft.lb/in弯曲降服强度+23℃ASTM D-79098.6MPa压缩应力+23℃@1%Def.ASTM D-69535.9MPa伸张强度-55℃ASTM D-638101MPa挠曲系数+23℃在25℃下2620MPa伸张强度+73℉ASTM D-63810.0MPsi压缩应力+73℉@10%DefASTM D-69518.0MPsi伸张强度+122℃ASTM D-63826.2MPa压缩应力+23℃@10%Def.ASTM D-695124MPa伸张强度+70℃ASTM D-6386.9MPa弯曲疲劳忍耐限度+23℃ASTM D-67132.4MPaIZOD冲击强度40℃ASTM D-25696.1j/m伸张强度+158℉ASTM D-6386.9MPsiIZOD冲击强度-40℉ASTM D-2561.8ft.lb/in洛氏硬度ASTM D-785M94,R120挠曲系数+122℃在25℃下620MPa弹性系数+73℉ASTM D-638450MPsi摩擦系数+73℉(+23℃)静态ThrustWasherTest30.20弹性系数+23℃ASTM D-6383100MPa断裂时之拉力伸张度-68℉(-55℃)ASTM D-63838%负载下之变形2000psi@+122℉(14Mpa@50℃)ASTM D-6210.5%伸张强度+23℃ASTM D-63868.9MPa无切口冲击程度+23℃ASTM D-256>5300(no break)j/mIZOD冲击强度+23℃ASTM D-256123j/m压缩应力+73℉@1%Def.ASTM D-6955.2MPsi电气性能绝缘强度Short Time,2.3mmASTM D-14919.7MV/m绝缘系数+73℉(+23℃)102to106HzASTM D-1503.7电弧抵抗力120mil(3.1mm)ASTM D-495220no trackingSec.绝缘强度Short Time,90 milsASTM D-149500V/mil电阻系数+73℉(+23℃)0.2%H2OASTM D-2571015ohm-cm热性能可燃烧性UL-9494HB线性热膨胀系数-40 to +85℉ASTM D-6965.810-5in/in.℉线性热膨胀系数+220 to +300℉ASTM D-6968.310-5in/in.℉热变形温度0.5MPaASTM D-648172℃线性热膨胀系数-40 to +29℃ASTM D-69610.410-5m/m.℃热传导系数2.6BTU-in/hr线性热膨胀系数+60 to +104℃ASTM D-69613.710-5m/m.℃热变形温度1.8MPaASTM D-648136℃热变形温度66psiASTM D-648342℉熔点ASTM D-2133175℃热变形温度264psiASTM D-648277℉熔点ASTM D-2133347℉线性热膨胀系数+29 to +60℃ASTM D-69612.210-5m/m.℃线性热膨胀系数+104 to +150℃ASTM D-69614.910-5m/m.℃线性热膨胀系数+85 to +140℉ASTM D-6966.810-5in/in.℉线性热膨胀系数+140 to +220℉ASTM D-6967.610-5in/in.℉热传导系数0.37W/mk